Boltaron 9200 - SOLIAO

About
Boltaron 9200 is a proprietary, extruded thermoplastic sheet, designed for use as aircraft window shades. Boltaron 9200 offers maximum light blocking characteristics, excellent impact strength, abrasion resistance, stain and chemical resistance, and thermoformability. Boltaron 9200 meets stringent FAA regulations for flammability, smoke generation and heat release as set forth in FAR 25.853 paragraphs (a) and (d). Boltaron 9200 is available as a single color (9200) or as a double color (9200C) construction. Colors: Custom Gauges: .047 to .060 Widths: Up to 48″ Lengths: Up to 120″ Textures: Coarse Matte (CM) Felt (FT) Haircell (HC) Levant (LT) Mesa (MS) Suede (SD)&&

About

Boltaron 9200 is a proprietary, extruded thermoplastic sheet, designed for use as aircraft window shades. Boltaron 9200 offers maximum light blocking characteristics, excellent impact strength, abrasion resistance, stain and chemical resistance, and thermoformability. Boltaron 9200 meets stringent FAA regulations for flammability, smoke generation and heat release as set forth in FAR 25.853 paragraphs (a) and (d). Boltaron 9200 is available as a single color (9200) or as a double color (9200C) construction. Colors: Custom Gauges: .047 to .060 Widths: Up to 48″ Lengths: Up to 120″ Textures: Coarse Matte (CM) Felt (FT) Haircell (HC) Levant (LT) Mesa (MS) Suede (SD)&&

Product Description
Generic	PMMA+PVC
Material Status	Commercial: Active
Features	The fouling resistance,High impact resistance,Good wear resistance,Solvent resistance
Availabilitys	North America
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.49	g/cm³	ASTM D792
Shrinkage rate
MD	0.50 to 0.70	%	ASTM D955

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	53 to 110	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, annealed	75.6 to 77.8	℃	ASTM D648

Supplementary information	Nominal value	Unit	Test method
Ds			ASTM F814
1.5 min	< 100		ASTM F814
4 min	< 200		ASTM F814
Forming temperature	168 to 185	℃

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	112 to 115		ASTM D785
tensile strength
yield	40.0 to 44.1	MPa	ASTM D638
Bending modulus	3030 to 3170	MPa	ASTM D790
bending strength
yield	68.9 to 72.4	MPa	ASTM D790

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
exothermic			FAR 25.853
2 min	< 65	kW·min/m²	FAR 25.853
Peak	< 65	kW/m²	FAR 25.853
12 sec	Pass
60 sec	Pass

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.