| About |
|---|
| This low density polyethylene is tailored for blown film applications that require: Superb optics Excellent impact strength Exceptional processability High coefficient of friction Typical blown film resin applications include: Produce bags Frozen food packaging Dry goods packaging Case shrink wrap, bundling Laminations General purpose clarity packaging&& |
| Product Description | |
|---|---|
| Supplier | Chevron Phillips |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | High Friction,Excellent Processability,High impact resistance,High anti-blocking,Low density |
| Availabilitys | North America,Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.925 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.80 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| Blown film | 0.57 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 32 | µm | |
| Drop hammer impact | |||
| 32 µ m, blow molded film | 110 | g | ASTM D1709 |
| Elmandorf tear strength | |||
| MD: 32 µ m, blow molded film | 230 | g | |
| TD: 32 µ m, blow molded film | 200 | g | |
| Oxygen transfer rate | |||
| 32 µ m, blow molded film | 5700 | cm³/m²/24 hr | ASTM D3985 |
| Water vapor transmittance | |||
| 32 µ m, blow molded film | 17 | g/m²/24 hr | ASTM F1249 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 99.0 | ℃ | ASTM D1525 |
| Melting peak temperature | 112 | ℃ | ASTM D3418 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60 °, 31.8 µ m, blow molded film | 127 | ASTM D2457 | |
| Haze | |||
| 31.8 µ m, blow molded film | 5.0 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |