| STYRON A-TECH™ 1210 is a newly developed high impact polystyrene (HIPS) resin based on patented technology, offering a unique combination of processability, stiffness, toughness, low gloss and surface smoothness. Main Characteristics: Low gloss and smooth sheet surface Ease of processing Excellent thermoforming behaviour Good blendability with GPPS Applications: Form Fill Seal (FFS) dairy packaging Medical device packaging Signage sheet Sheet applications requiring matt and smooth surface Complies with: Europe Regulation (EC) 10/2011 U.S. FDA 21 CFR 177.1640 Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PS (HIPS) |
| Material Status | Commercial: Negative |
| Features | Good Rigidity,Excellent Processability,Good flexibility,Good surface appearance,Low Gloss |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.04 | g/cm³ | ASTM D792 |
| 23℃ | 1.04 | g/cm³ | ISO 1183 |
| Apparent density | 0.60 | g/cm³ | ISO 60 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 3.4 | g/10min | ASTM D1238 |
| 200℃，5.0kg | 3.4 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 1750 | MPa | ASTM D638 |
| — | 1750 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 19.5 | MPa | ASTM D638 |
| yield | 19.5 | MPa | ISO 527-2/5 |
| fracture | 22.0 | MPa | ASTM D638 |
| fracture | 22.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 65 | % | ASTM D638 , ISO 527-2 |
| Bending modulus | |||
| — | 1950 | MPa | ASTM D790 |
| — | 1950 | MPa | ISO 178 |
| bending strength | |||
| — | 38.0 | MPa | ASTM D790 |
| — | 38.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 14 | kJ/m² | ISO 180/4A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 98.0 | ℃ | ISO 306/A120 , ASTM D1525 5 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Procedure B |
| 3. 0.20 in/min |
| 4. Method I (3 point load), 0.051 in/min |
| 5. Rate B (120°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |