LEXAN™ FL933 resin

About
30% 玻纤增强，出色的抗弯强度和模量;良好的抗拉强度，紫外线稳定。

Product Description
Supplier	SABIC
Generic	Polycarbonate
Material Status	Commercial: Active
Features	Weather resistance is good,Glass fiber reinforced
Availabilitys	North America

Technical Data
MECHANICAL	Nominal value	Unit	Test method
tensile strength
Yield, 6.35 mm	73	MPa
Tensile strain
Fracture, 6.35 mm	3	%
Tensile modulus
6.40 mm	7060	MPa
bending strength
Yield, 6.40 mm	130	MPa
Bending modulus
6.40 mm	7030	MPa

IMPACT	Nominal value	Unit
Foam
Electric 6.4 mm Wt reduction	20	%
Physical 6.4 mm Wt reduction	10	%
Hot 6.4 mm Wt reduction	10	%
Mechanical 6.4 mm Wt reduction	10	%
Impact 6.4 mm Wt reduction	10	%
Notched impact strength of cantilever beam
23℃	490	J/m
Falling dart impact
23℃	42	N.m

THERMAL	Nominal value	Unit
Hot deformation temperature
1.8 MPa, unannealed, 3.2 mm	138	℃
0.45 MPa, unannealed, 3.2 mm	143	℃
Linear coefficient of thermal expansion
MD：-40~95℃	2.16E-05	1/℃
specific heat	1.04	J/g-℃
Thermal conductivity	0.16	W/m-℃

PHYSICAL	Nominal value	Unit
Density	1.43
Foam forming	1.29
Water absorption rate
24hr	0.12	%
Water absorption rate
Equilibrium, 23 ℃	0.26	%
Shrinkage rate
MD：6.4 mm	0.2 – 0.4	%

Electrical performance	Nominal value	Unit
Volume resistivity	2.4E+17	ohms·cm
Surface resistivity	>1.1E+17	ohms
Relative permittivity
100 Hz	2.7
Relative permittivity
1 MHz	2.61
Dissipation factor
100 Hz	0.0034
Dissipation factor
1 MHz	0.0075

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Extreme oxygen index
LOI	40.4	%

Process Conditions
Structural foam molding	Nominal value	Unit	Test method
Foaming agent, physical system	氮气
Foaming agent, chemical system	FLC95
Drying time (foaming agent)	4	hrs
Drying temperature (foaming agent)	105	°C
Concentration range (foaming agent)	3 – 5	%
Recommended concentration (foaming agent)	1.5	%
Drying temperature (resin)	120	°C
Drying time (resin)	3 – 4	hrs
Drying time (resin, cumulative)	48	hrs
Melt temperature	290 – 315	°C
Nozzle temperature	270 – 295	°C
Front temperature	295- 310	°C
Mid section temperature	295 – 310	°C
Post stage temperature	255 – 265	°C
Mold temperature	70 – 95	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.