| About |
|---|
| SUMIKATHENE® F218-0 is a Low Density Polyethylene material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary attribute of SUMIKATHENE® F218-0: High Strength. Typical application of SUMIKATHENE® F218-0: Film&& |
| Product Description | |
|---|---|
| Supplier | Sumitomo |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.919 | g/cm³ | JIS K6922-1 |
| Melt Flow Rate | 1.0 | g/10min | JIS K6922-1 |
| ESCR(Environmental Stress Cracking Resistance) | 3.50 | hr | ASTM D1693 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile impact strength | 340 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 90.0 | ℃ | JIS K7206 |
| Melting temperature | 108 | ℃ | DSC |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 53 | JIS K7215 | |
| tensile strength | |||
| fracture | 16.0 | MPa | Internal Method |
| Tensile strain | |||
| fracture | 700 | % | Internal Method |
| Bending modulus | |||
| 23℃ | 195 | MPa | ASTM D747 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |