| REPOL Polypropylene R200MK is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity stereospecific catalyst system. Repol R200MK is recommended for use in Injection Moulding & Stretch Blow Moulding processes. It is an ideal material for attaining high clarity in housewares, syringes and ISBM products. Repol R200MK contains clarifier and antistatic agent that reduces static charge buildup on products.&& |
| Product Description | |
|---|---|
| Supplier | Reliance |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good Clarity,Random copolymer,Antistatic property |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 230℃，2.16kg | 20 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 25.0 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 10 | % | ASTM D638 |
| Bending modulus | |||
| 1% secant | 900 | MPa | ASTM D790-A |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 60 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 90.0 | ℃ | ASTM D648 |
| Melting temperature | 135 | ℃ | DSC |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 2.0 in/min |
| 3. Type I |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |