| About |
|---|
| DAI-EL G-7210BP is a bisphenol curable, gum copolymer. It is designed especially for injection molding of seals. Properly compounded, DAI-EL G-7210BP produces vulcanizates with excellent heat and compression set resistance.&& |
| Product Description | |
|---|---|
| Supplier | Daikin Fluorochemicals |
| Generic | 氟橡胶 |
| Material Status | Commercial: Active |
| Features | High Heat Resistance,Baking,Copolymer |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.81 | g/cm³ | |
| Mooney viscosity | |||
| ML 1+10，121℃ | 28 | MU | |
| Fluorine content | 66 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 75 | ||
| Shaw’s A | 76 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 100% strain, 25 ℃ | 5.50 | MPa | |
| 100% strain, 25 ℃ | 5.40 | MPa | |
| tensile strength | |||
| Yield, 25 ℃ | 12.5 | MPa | |
| Yield, 25 ℃ | 13.0 | MPa | |
| Tensile strain | |||
| Fracture, 25 ℃ | 220 | % | |
| Fracture, 25 ℃ | 210 | % | |
| Compression deformation | ASTM D395B | ||
| 200℃，70 hr | 19 | % | ASTM D395B |
| 200℃，70 hr | 18 | % | ASTM D395B |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Low temperature brittleness | |||
| TR10 | -18 | ℃ | ASTM D1329 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. ODR |
| 3. MDR 2000 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |