| Kingfa FRHIPS-113 is a General Purpose Polystyrene material. It is available in Asia Pacific or North America for gas-assisted injection molding or injection molding. Important attributes of Kingfa FRHIPS-113 are: Flame Rated Flame Retardant Heat Resistant Typical application of Kingfa FRHIPS-113: Housings&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PS (HIPS) |
| Material Status | Commercial: Active |
| Features | High impact resistance,Flame Characteristics |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.15 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.40-0.60 | % | ASTM D995 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 6.0 | g/10min | ASTM D1238 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 78.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| 99.0 | ℃ | ASTM D1525 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+16 | Ω.cm | ASTM D257 |
| Surface resistance | 1.0E+16 | Ω.cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50mm | V-0 | UL 94 | |
| 3.00mm | V-0 | UL 94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 110 | J/m | ASTM D256 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 97 | R 级 | ASTM D785 |
| tensile strength | |||
| 23℃ | 27.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 45 | % | ASTM D638 |
| bending strength | |||
| 23℃ | 40.0 | MPa | ASTM D790 |
| Bending modulus | |||
| 23℃ | 2200 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. 4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |