| About |
|---|
| Jamplast JPAH is an Acetal (POM) Homopolymer material. It is available in North America for cast film, extrusion, injection molding, profile extrusion, or sheet extrusion. Important attributes of Jamplast JPAH are: Flame Rated High Viscosity Lubricated Wear Resistant Typical applications include: Engineering/Industrial Parts Film Hose/Tubing Sheet Wire & Cable&& |
| Product Description | |
|---|---|
| Generic | Paraformaldehyde |
| Material Status | Commercial: Active |
| Features | High Viscosity,Low coefficient of friction,Lubricating,Good wear resistance,HB |
| Availabilitys | North America |
| Process Methods | Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.53 | g/cm³ | ASTM D792 |
| Water absorption rate | ASTM D570 | ||
| 23℃，24hr | 0.20 | % | ASTM D570 |
| Saturation, 23 ℃ | 0.72 | % | ASTM D570 |
| Equilibrium, 23 ℃, 50% RH | 0.18 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 2910 | MPa | ASTM D638 |
| tensile strength | |||
| 23℃ | 50.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 11 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 2710 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 31 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 490 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 163 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 95.0 | ℃ | ASTM D648 |
| Melting temperature | 178 | ℃ | DSC |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD：23~54℃ | 1.0E-4 | 1/℃ | ASTM E831 |
| TD：23~54℃ | 1.0E-4 | 1/℃ | ASTM E831 |
| 1.5 mm | 105 | ℃ | UL 746 |
| 3.0 mm | 105 | ℃ | UL 746 |
| 1.5 mm | 85.0 | ℃ | UL 746 |
| 3.0 mm | 85.0 | ℃ | UL 746 |
| Relative temperature index | UL 746 | ||
| Electrical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 1.50 mm | 90.0 | ℃ | UL 746 |
| 3.00 mm | 90.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Recommended maximum moisture content | 0.20 | % | |
| Processing (melt) temperature | 210 to 220 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |