| About |
|---|
| TORZEN® HV240AHSL NC01 is a high viscosity PA66 resin for extrusion and injection molding applications. It is heat stabilized and lubricated. Available in natural and black.&& |
| Product Description | |
|---|---|
| Supplier | INVISTA |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | High Viscosity,Lubricating,Heat Stabilized |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：2.0 mm | 1.8 | % | ISO 294-4 |
| MD：2.0 mm | 1.7 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | 2.0 | % | ISO 62 |
| Viscosity (H2SO4 (sulfuric acid)) | 290 | cm³/g | ISO 307 |
| Relative viscosity | |||
| 1% sulfuric acid | 5 | ||
| in formic acid，nominal | 240 | ASTM D789 | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3200 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 84.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 35 | % | ISO 527-2 |
| yield | 4.2 | % | ISO 527-2 |
| Bending modulus | 3200 | MPa | ISO 178 |
| bending strength | 102 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 5.2 | kJ/m² | ISO 179 |
| 23℃ | 4.4 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -30℃ | No Break | ISO 179 | |
| 23℃ | No Break | ISO 179 | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 5.3 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 69.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 209 | ℃ | ISO 75-2/B |
| Melting temperature | 262 | ℃ | ISO 11357-3 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.010 to 0.080 | % | |
| Barrel rear temperature | 250 to 270 | °C | |
| Barrel middle temperature | 270 to 290 | °C | |
| Barrel front temperature | 270 to 290 | °C | |
| Nozzle temperature | 270 to 290 | °C | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 50 to 90 | °C | |
| Back pressure | 0.200 to 1.00 | MPa | |
| Screw speed | 75 to 180 | rpm | |
| Cushion | 4.00 to 6.00 | mm | |
| Vent depth | 7.0E-3 to 0.040 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |