| Polypropylene homopolymer talcum filled 10%. Available: all colors, UV stabilized (L), heat stabilized (H), laser printable (LP), detergent stabilized (D).&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Laser engraving,Heat Stabilized,Homopolymer,Resistance to detergents,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.00 to 1.02 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 12 | g/10min | ASTM D1238，ISO 1133 |
| Shrinkage rate | ASTM D955 | ||
| MD | 1.2 | % | ASTM D955 |
| TD | 1.2 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.050 | % | ASTM D570，ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 30.0 | MPa | ASTM D638 , ISO 527-2 |
| Tensile strain | |||
| fracture | 45 | % | ASTM D638 , ISO 527-2 |
| Bending modulus | 2200 | MPa | ASTM D790 , ISO 178 |
| bending strength | |||
| — | 45.0 | MPa | ISO 178 |
| fracture | 45.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 35 | J/m | ASTM D256 , ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 75.0 | ℃ | ASTM D648，ISO 75-2/A |
| Vicat Softening Temp | |||
| — | 155 | ℃ | ASTM D1525 2 , ISO 306/A 2 |
| — | 90.0 | ℃ | ASTM D1525 3 , ISO 306/B 3 |
| Linear coefficient of thermal expansion | |||
| MD | 6.0E-5 | 1/℃ | ASTM D696 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | HB | UL 94 | |
| Glowing wire flammability index | |||
| 1.0 mm | 650 | ℃ | IEC 60695-2-12 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 70 to 80 | °C | |
| Drying time | 1.0 | hr | |
| Processing (melt) temperature | 190 to 220 | °C | |
| Mold temperature | 30 to 50 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 3. Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |