| About |
|---|
| LNP LUBRICOMP UL002S is a compound based on Polypthalamide resin containing 10% PTFE. Added features of this grade include: Heat Stabilized, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound UL-4020 HS Product reorder name: UL002S&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Lubricating,Good wear resistance,Heat Stabilized |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.25 | g/cm³ | ASTM D792 |
| Density | 1.26 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD：24 hrs | 0.70 to 0.90 | % | ASTM D955 |
| MD：24 hrs | 0.90 to 2.0 | % | ASTM D955 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.73 | % | ISO 62 |
| 24hr，50% RH | 0.47 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3170 | MPa | ASTM D638 |
| Tensile modulus | 3220 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 60.0 | MPa | ISO 527-2/5 |
| fracture | 60.0 | MPa | ASTM D638 |
| yield | 60.0 | MPa | ASTM D638 |
| yield | 58.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 2.2 | % | ASTM D638 |
| fracture | 2.2 | % | ISO 527-2/5 |
| yield | 2.2 | % | ASTM D638 |
| yield | 2.2 | % | ISO 527-2/5 |
| Bending modulus | |||
| 50 mm span | 2980 | MPa | ASTM D790 |
| bending strength | |||
| Fracture, 50 mm span | 105 | MPa | ASTM D790 |
| Yield, 50 mm span | 105 | MPa | ASTM D790 |
| friction coefficient | ASTM D3702 Modified | ||
| dynamic | 0.27 | ASTM D3702 Modified | |
| static state | 0.17 | ASTM D3702 Modified | |
| Wear factor | ASTM D3702 Modified | ||
| Ring | -0.100 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Washer | 20.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 450 | J/m | ASTM D4812 |
| 23℃ | 2.7 | kJ/m² | ISO 180-1A |
| 23℃ | 26 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 27 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 2.80 | J | ASTM D3763 |
| Multi axial instrumented impact energy | 0.500 | J | ISO 6603-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Barrel rear temperature | 310 to 321 | °C | |
| Barrel middle temperature | 316 to 327 | °C | |
| Barrel front temperature | 327 to 338 | °C | |
| Processing (melt) temperature | 316 to 332 | °C | |
| Mold temperature | 149 to 171 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |