| Monprene OM-10268 is a specialty thermoplastic elastomer, available in NAT, BLK, and colors, designed for overmolding and co-extrusion applications like grips and anti-skid parts for consumer and industrial products. Monprene OM-10268 is a medium hardness, low density, opaque grade that exhibits excellent adhesion to PC, ABS, and PC/ABS.&& |
| Product Description | |
|---|---|
| Supplier | Teknor Apex |
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,Smoothness,Good bond,Moderate liquidity,Good wear resistance,Solvent resistance,Agglomerability,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Multiple injection molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.998 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 10 | g/10min | ASTM D1238 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| TD, 100% strain | 2.25 | MPa | ASTM D412 |
| MD, 100% strain | 2.78 | MPa | ASTM D412 |
| tensile strength | ASTM D412 | ||
| TD, 300% strain | 3.73 | MPa | ASTM D412 |
| MD, 300% strain | 4.22 | MPa | ASTM D412 |
| tensile strength | ASTM D412 | ||
| fracture | 6.74 | MPa | ASTM D412 |
| MD, fracture | 6.16 | MPa | ASTM D412 |
| Tensile strain | ASTM D412 | ||
| fracture | 570 | % | ASTM D412 |
| Flow rate, fracture | 520 | % | ASTM D412 |
| tear strength | ASTM D624 | ||
| TD | 30.5 | kN/m | ASTM D624 |
| MD | 30.5 | kN/m | ASTM D624 |
| Compression deformation | ASTM D395B | ||
| 23℃，22 hr | 38 | % | ASTM D395B |
| 70℃，22 hr | 17 | % | ASTM D395B |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shaw’s A | 70 | ASTM D2240 | |
| Shore A, 5 seconds | 68 | ASTM D2240 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative temperature index | |||
| Electrical performance | 50.0 | ℃ | UL 746 |
| Strength mechanical performance | 50.0 | ℃ | UL 746 |
| Impact mechanical performance | 50.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.0 to 1.2 mm，All Colors | HB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Adhesion to ABS | |||
| Adhesion to PC | |||
| Adhesion to PC/ABS |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 60 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 138 to 188 | °C | |
| Barrel middle temperature | 154 to 199 | °C | |
| Barrel front temperature | 154 to 216 | °C | |
| Nozzle temperature | 154 to 221 | °C | |
| Processing (melt) temperature | 166 to 221 | °C | |
| Mold temperature | 10 to 32 | °C | |
| Injection pressure | 1.38 to 5.52 | MPa | |
| Injection speed | Moderate-Fast | ||
| Back pressure | 0.172 to 0.862 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Cushion | 3.81 to 25.4 | mm | |
| Drying temperature | 60 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel 1 zone temperature | 138 to 149 | °C | |
| Barrel 2 zone temperature | 149 to 160 | °C | |
| Barrel 3 zone temperature | 160 to 182 | °C | |
| Barrel 4 zone temperature | 160 to 182 | °C | |
| Nozzle temperature | 160 to 182 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C, 20 in/min |
| 3. Type 1 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |