| About |
|---|
| Kraton D1157 E is a clear, linear block copolymer based on styrene and butadiene with bound styrene of 29.5% mass. It is supplied from Europe in the physical form(s) identified below in the grade nomenclature: Kraton D1157 ES – supplied as porous pellets dusted with amorphous silica Kraton D1157 ETM – supplied as powder dusted with talc for the North American market Kraton D1157 E is used as a modifier of bitumen or thermoplastics and in compound formulations. It may also find use as an ingredient in formulating adhesives, sealants and coatings.&& |
| Product Description | |
|---|---|
| Generic | SBS |
| Material Status | Commercial: Active |
| Features | Inoxidizability,Copolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.940 | g/cm³ | ISO 2781 |
| Apparent density | 0.40 | g/cm³ | ASTM D1895B |
| Melt Flow Rate | |||
| 200℃，5.0kg | 3.5 to 6.5 | g/10min | ISO 1133 |
| Antioxidant Additive | > 0.15 | % | Internal Method |
| Polystyrene content | 29 to 31 | % | Internal Method |
| Total Extractables | < 1.0 | % | Internal Method |
| Ash Content | |||
| ES | 0.10 to 0.40 | % | ISO 247 |
| ETM | 4.0 to 6.0 | % | Internal Method |
| Volatiles | < 0.30 | % | Internal Method |
| Solution viscosity | |||
| 25wt% toluene, 25 ℃ | 1.3 to 1.9 | Pa·s | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 15 seconds, molded | 70 | ASTM D2240 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 28.0 | MPa | ISO 37 |
| 300% strain | 2.90 | MPa | ISO 37 |
| Tensile strain | |||
| fracture | 800 | % | ISO 37 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 25%w in toluene solution at 25°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |