| Halogen and phosphorus free flame retardant injection molding type with high heat stabilization i.e. for electrical components |
| Product Description | |
|---|---|
| Generic | PA66/6 |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,Copolymer,Low to no phosphorus content,Heat Stabilized |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| 23℃ | 1.15 | g/cm³ | |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 2.2 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 3400 | MPa | |
| Tensile stress (yield, 23 ° C) | 80.0 | MPa | |
| Tensile strain | |||
| Yield, 23 ℃ | 4.5 | % | |
| Nominal tensile fracture strain (23 ° C) | 20 | % |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 5.0 | kJ/m² | |
| 23℃ | 7.0 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| 23℃ | 无断裂 | ||
| Impact strength of cantilever beam notch | |||
| -30℃ | 3.0 | kJ/m² | |
| 23℃ | 5.0 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 215 | ℃ | |
| 1.8 MPa, unannealed | 80.0 | ℃ | |
| Melting temperature | 262 | ℃ | |
| Operating temperature | |||
| 20 000 hours | 130 | °C | |
| Some hours | 185 | °C |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+14 | ohms | |
| Volume resistivity | 1.0E+14 | ohms·cm | |
| Relative permittivity | |||
| 1 MHz | 3.50 | ||
| Compared to the leakage tracing index | 600 | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.40 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glowing wire flammability index | |||
| 0.8-1.6 mm | 960 | ℃ | |
| Hot filament ignition temperature (0.8 to 1.6 mm) | 775 | °C |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 260 to 280 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |