| About |
|---|
| Borstar FB1350 is a linear medium density polyethylene grade combining excellent extrusion properties with high film stiffness. Borstar FB1350 is well suited for mono- and coextrusion of films produced with high neck or low neck extrusion. Borstar FB1350 contains antioxidant.&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | MDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Renewable resources,Inoxidizability |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.935 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，21.6kg | 15 | g/10min | ISO 1133 |
| 190℃，5.0kg | 0.60 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | 0.40 | ISO 8295 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Tensile modulus | ISO 527-3 | ||
| MD | 500 | MPa | ISO 527-3 |
| TD | 650 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD | 57.0 | MPa | ISO 527-3 |
| TD | 48.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture | 400 | % | ISO 527-3 |
| TD, fracture | 650 | % | ISO 527-3 |
| Drop hammer impact | 150 | g | ISO 7765-1 |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD | 12.0 | kN/m | ISO 6383-2 |
| TD | 290.0 | kN/m | ISO 6383-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 127 | ℃ | ISO 11357-3 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 20° | 5 | ASTM D2457 | |
| Haze | 80 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Puncture resistance | |||
| Energy to Resist | 150 | J/cm | ISO 7765-2 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 190 to 210 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |