| About |
|---|
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Availabilitys | North America |
| Process Methods | Foam treatment |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| proportion | |||
| –² | 0.878 | g/cm³ | ASTM D792 |
| — | 1.10 | g/cm³ | ASTM D792 |
| Forming shrinkage rate | |||
| MD | 0.60 – 0.80 | % | Internal Method |
| Water absorption rate | |||
| 24hr | % | ASTM D570 | |
| Saturation, 23 ℃ | % | ASTM D570 | |
| Outdoor adaptability | f1 | UL 746C | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 6.35mm | 29.0 | MPa | ASTM D638 |
| elongation at break | |||
| Fracture, 6.35mm | 12 | % | ASTM D638 |
| Bending modulus | |||
| 6.40mm | 1900 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 6.40mm | 61.4 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 23°C, 6.40 mm | 200 | J/m | ASTM D4812 |
| Dart impact equipped with measuring instruments | |||
| -30 ° C, peak load energy | 3.28 | J | ASTM D3763 |
| 23 ° C, peak load energy | 11.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, 6.40 mm, unannealed | 88.9 | ℃ | ASTM D648 |
| 1.8 MPa, 6.40 mm, unannealed | 76.7 | ℃ | ASTM D648 |
| Relative temperature index | |||
| Electrical performance | 85.0 | ℃ | UL 746 |
| Mechanical impact performance | 85.0 | ℃ | UL 746 |
| Non mechanical impact performance | 85.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+17 | ohm | ASTM D257 |
| Dielectric strength | |||
| 1.60 mm in oil | 12 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1 MHz | 2.20 | ASTM D150 | |
| Dissipation factor | |||
| 1 MHz | 4.4E-3 | ASTM D150 | |
| Arc resistance | PLC 6 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 1 | UL 746 | |
| High voltage arc marking rate | PLC 4 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.00 mm | V-1 | UL 94 | |
| 5.99 mm | V-0 | UL 94 | |
| 3.91 mm | 5VA | UL 94 | |
| Foam – Flame class minimum density | 0.850 | g/cm³ | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| Structural foam molding | Nominal value | Unit | Test method |
| Concentration range (foaming agent) | 1 – 3 | % | |
| Drying temperature (resin) | 71 – 82 | ℃ | |
| Drying time (resin) | 2 – 4 | hrs | |
| Accumulated drying time (resin) | 8 | hrs | |
| Front temperature | 271 – 304 | ℃ | |
| Mid section temperature | 271 – 304 | ℃ | |
| Post stage temperature | 232 – 260 | ℃ | |
| Melting temperature | 271 – 310 | ℃ | |
| Mold temperature | 27 – 54 | ℃ | |
| Nozzle temperature | 271 – 304 | ℃ | |
| Recommended concentration (foaming agent) | 2 | % | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |