| Product Description | |
|---|---|
| Supplier | Kolon |
| Generic | TPEE |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.16 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 240℃，2.16kg | 36 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 40 | ISO 868 | |
| tensile strength | 20 | MPa | ISO 527 |
| Tensile strain | |||
| fracture | 600 | % | ISO 527 |
| Bending modulus | 72 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -40℃ | 未断裂 | ISO 179/1eA | |
| 23℃ | 未断裂 | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| melting point | 178 | ℃ | ISO 11357-1 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Processing temperature | Nominal value | Unit | Test method |
| drying temperature | 80-110 | ℃ | |
| Drying time | 3-6 | hrs | |
| Temperature at the rear of the barrel | 160-170 | ℃ | |
| Temperature in the middle of the barrel | 170-190 | ℃ | |
| Front temperature of material barrel | 185-220 | ℃ | |
| Nozzle temperature | 200-220 | ℃ | |
| Mold temperature | 20-40 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |