| About |
|---|
| 注塑成型，50%玻纤增强，耐热老化 |
| Product Description | |
|---|---|
| Supplier | LANXESS |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.57 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 290℃，5 kg | 19 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：150x105x3，300℃ / MT 80℃，400 bar | 0.23 | % | ISO 2577 |
| Normal, 150x105x3300 ℃/MT 80 ℃, 400 bar | 1.25 | % | ISO 2577 |
| Post contraction | |||
| Parallel, 150x105x3; 120 ℃; 4 hours | 0.02 | % | ISO 2577 |
| 正常,150x105x3; 120 °C; 4 h | 0.03 | % | ISO 2577 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 1 mm/min | 10700 | MPa | ISO 527-1 |
| Fracture stress | |||
| 5 mm/min | 170 | MPa | ISO 527-1 |
| Fracture strain | |||
| 5 mm/min | 4.0 | % | ISO 527-1 |
| Bending modulus | |||
| 2 mm/mim | 14000 | MPa | ISO 178 |
| bending strength | |||
| 2 mm/min | 370 | MPa | ISO 178 |
| Bending strain | |||
| 2 mm/min | 3.0 | % | ISO 178 |
| bending strength | |||
| 3.50% strain, 2 mm/min | 235 | MPa | ISO 178 |
| ball indentation hardness | 290 | N/mm² | ISO 2039-1 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| 10℃ / min | 263 | ℃ | ISO 11357-1 |
| Hot deformation temperature | |||
| 1.8 MPa | 250 | ℃ | ISO 75-1/2 |
| 0.45 MPa | 250 | ℃ | ISO 75-1/2 |
| Vicat Softening Temp | |||
| B120 | >230 | ℃ | ISO 306 |
| Flame retardant level | |||
| 1.60 mm | HB | 等级 | UL 94 |
| 3.20 mm | HB | 等级 | UL 94 |
| Extreme oxygen index | 27 | % | ISO 4589-2 |
| Glowing wire flammability index | |||
| 2.0 mm | 600 | ℃ | IEC 60695-2-12 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative permittivity | |||
| 100 Hz | 4.5 | IEC 60250 | |
| 1 MHz | 4.0 | IEC 60250 | |
| Loss factor | |||
| 100 Hz | 90 | 10 -4 | IEC 60250 |
| 1 MHz | 150 | 10 -4 | IEC 60250 |
| Volume resistivity | 1E+15 | ohms·cm | IEC 60093 |
| Surface resistivity | 1.0E+14 | ohms | IEC 60093 |
| Medium strength | |||
| 1 mm | 40 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | |||
| Solution A | 375 | IEC 60112 | |
| Solution B | 225M | IEC 60112 |
| Other performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Water absorption rate | |||
| Static, 23 ℃ | 4 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 1.4 | % | ISO 62 |
| Fiberglass content | 50 | % | ISO 3451-1 |
| bulk density | 700 | kg/m³ | ISO 60 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 19 | kJ/m² | ISO 179-1eA |
| -30℃ | 15 | kJ/m² | ISO 179-1eA |
| Charpy impact strength | |||
| 23℃ | 95 | kJ/m² | ISO 179-1eU |
| -30℃ | 100 | kJ/m² | ISO 179-1eU |
| Impact strength of cantilever beam notch | |||
| 23℃ | 14 | kJ/m² | ISO 180-1A |
| -30℃ | 11 | kJ/m² | ISO 180-1A |
| Process Conditions | |||
|---|---|---|---|
| Processing suggestions | Nominal value | Unit | Test method |
| Sample processing conditions | Nominal value | Unit | Test method |
| Melt temperature | 300 | °C | ISO 294 |
| Mold temperature | 80 | °C | ISO 294 |
| Drying temperature | 80 | °C | |
| Drying time | 2-6 | h | |
| Remaining moisture content | 0.03-0.12 | % | |
| Melt temperature | 280-300 | °C | |
| Mold temperature | 80-120 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |