| About |
|---|
| ELITE™ 5815P is produced via INSITE™ Technology from Dow. It is an ethylene alpha-olefin resin for monolayer and coextrusion coating that offers excellent low temperature seal initiation, ultimate seal strength, hot tack strength and good taste and odor performance. Monolayer and coextrusion coating for packaging applications. Coextruded with PRIMACOR™ copolymer as a cost effective foil or PET sealant. Complies with U.S. FDA FCN 424 Complies with EU. No 10/2011 Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | EPE |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.910 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 15 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Initial sealing temperature | 90.6 | ℃ | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| DSC | 124 | ℃ | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 260 to 316 | °C | |
| Shrinkage (316°C, 25.4 μm) | 235.0 | mm | |
| Minimum coating thickness | < 7.6 | µm | |
| Minimum coating weight | < 7.3 | g/m² | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. – Coating onto PET/poly/foil/0.5 mil acid copolymer – Temperature at which 1 lb/in (4.4 FN/25.4 mm) heat seal strength is achieved. – Heat Seal Strength, Topwave HT Tester, 0.5 S dwell, 40 psi bar pressure, 10 in/min pull speed. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |