ELITE™ 5400G Enhanced Polyethylene Resin is a copolymer produced via INSITE™ Technology from Dow. It offers a unique combination of low seal initiation, moderate stiffness and low blocking tendencies for good performance on automated packaging equipment. For food and specialty packaging films Extremely high impact resistance and good tear properties Good optical properties Complies with: U.S. FDA FCN 424 EU, No 10/2011 Canadian HPFB No Objection Consult the regulations for complete details.&&

About

ELITE™ 5400G Enhanced Polyethylene Resin is a copolymer produced via INSITE™ Technology from Dow. It offers a unique combination of low seal initiation, moderate stiffness and low blocking tendencies for good performance on automated packaging equipment. For food and specialty packaging films Extremely high impact resistance and good tear properties Good optical properties Complies with: U.S. FDA FCN 424 EU, No 10/2011 Canadian HPFB No Objection Consult the regulations for complete details.&&

Product Description
Supplier	DOW
Generic	EPE
Material Status	Commercial: Active

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.916	g/cm³	ASTM D792
Melt Flow Rate
190℃，2.16kg	1.0	g/10min	ASTM D1238

film	Nominal value	Unit	Test method
film thickness
test	25	µm
Membrane puncture strength	6.67	J	Internal Method
Membrane puncture force	68.9	N	Internal Method
Membrane puncture resistance	32.3	J/cm³	Internal Method
Membrane strength			ASTM D882
MD	83.6	J/cm³	ASTM D882
TD	95.1	J/cm³	ASTM D882
Secant modulus			ASTM D882
1% secant, MD	218	MPa	ASTM D882
2% secant, MD	188	MPa	ASTM D882
1% secant, TD	251	MPa	ASTM D882
2% secant, TD	209	MPa	ASTM D882
tensile strength			ASTM D882
MD, yield	10.4	MPa	ASTM D882
TD, yield	10.5	MPa	ASTM D882
MD, fracture	38.5	MPa	ASTM D882
TD, fracture	36.3	MPa	ASTM D882
Tensile strain			ASTM D882
MD, fracture	450	%	ASTM D882
TD, fracture	630	%	ASTM D882
Drop hammer impact	1000	g	ASTM D1709B
Elmandorf tear strength			ASTM D1922
MD	280	g	ASTM D1922
TD	600	g	ASTM D1922

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	104	℃	ASTM D1525
Melting temperature
DSC	123	℃	Internal Method

optical performance	Nominal value	Unit	Test method
gloss
45°	32		ASTM D2457
Haze	20	%	ASTM D1003

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.