| About |
|---|
| 无卤阻燃V-0,优异的机械性能，高耐热，耐化学药品 |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Halogen free,High Heat Resistance,Solvent resistance |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | |||
| 50 mm/min | 60 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 50 mm/min | 50 | % | ASTM D638 |
| bending strength | |||
| 2 mm/min | 90 | MPa | ASTM D790 |
| Bending modulus | |||
| 2 mm/mim | 2500 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Load deformation temperature | |||
| 1.8MPa，6.4mm | 93 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistance | 10^16 | Ω | ASTM D257 |
| Dielectric strength | |||
| 1.6 mm | 28 | kV/mm | ASTM D149 |
| other | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0，5VB | UL 94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 550 | J/m | ASTM D256 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melt Flow Rate | |||
| 260℃，2.16kg | 18 | g/10min | ASTM D1238 |
| Shrinkage rate | 0.4-0.6 | % | ASTM D955 |
| Density | 1.19 | g/cm³ | ASTM D792 |
| Process Conditions | |||
|---|---|---|---|
| Typical processing conditions | Nominal value | Unit | Test method |
| Melt temperature | 230~275 | °C | |
| Temperature of the rear section of the barrel | 220~255 | °C | |
| Temperature in the middle section of the barrel | 220~275 | °C | |
| Temperature of the front section of the material barrel | 240~280 | °C | |
| Mold temperature | 40~100 | °C | |
| Upper limit of processing temperature | 280 | °C | |
| Injection molding speed | 低to高 | ||
| Pre-drying | 90-100°C,3-6hrs | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |