| About |
|---|
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good tear strength,weathering resistance,Solvent resistance,Good wear resistance,Good flexibility |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt index | |||
| 5.0 kg | 0.23 | g/10min | ISO 1133 |
| 21.6 kg | 6.4 | g/10min | ISO 1133 |
| Density | 0.959 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile stress | |||
| 23℃，50 mm/min | 23 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | ≥350 | % | ISO 527-2 |
| Yield, 23 ℃, 50 mm/min | 8 | % | ISO 527-2 |
| Tensile modulus | 1100 | MPa | ISO 527-2 |
| Bending modulus | |||
| 4-point loading / 1 min | 1200 | MPa | DIN 16841 |
| 4-point loading / 24 hrs | 560 | MPa | DIN 16841 |
| 4-point loading / 2000 hrs | 330 | MPa | DIN 16841 |
| Tensile creep modulus | |||
| 1 hour /2 MPa | 850 | MPa | ASTM D899 |
| 1000 hours /2 MPa | 360 | MPa | ASTM D899 |
| 10 | MPa | ISO 9080 | |
| Full Notch Transformation Test (FNCT) | |||
| 4.0 MPa, 2% Arkopal N100, 80℃ | ＞1000 | hour(s) | ISO 16770 |
| Shore hardness | |||
| Shore D, 3 sec | 63 | ISO 868 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 26 | kJ/m² | ISO 179-1/1eA |
| -30℃ | 13 | kJ/m² | ISO 179-1/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| 210℃ | ≥20 | minute(s) | ISO 868 |
| Vicat Softening Temp | 74 | ℃ | ISO 11357-6 |
| DSC melting point | 129 | ℃ | DSC |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Carbon black content | 2.25 | % | ISO 6964 |
| Odor threshold | |||
| Measured at particle/30 * C/4h extraction time | ＜2 | EN 1622/EN 1420 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |