| About |
|---|
| Flexible NORYL injection molding grade. Low specific gravity with very good non-halogenated flame retardant performance. Developed for evaluation in overmolding applications such as plugs, strain relief”s, and connectors. UL94 V-0 performance with good processability.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+TPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good flexibility,Halogen free,Flame Characteristics,Low density,V-0 |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 210℃，5.0kg | 15 | g/10min | ASTM D1238 |
| 250℃，2.16kg | 20 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| TD：24 hrs | 1.1 | % | ASTM D955 |
| MD：24 hrs | 1.1 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.10 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 30 seconds | 78 | ASTM D2240 | |
| tensile strength | |||
| fracture | 8.00 | MPa | ISO 527-2/50 |
| fracture | 7.50 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 170 | % | ASTM D638 |
| fracture | 170 | % | ISO 527-2/50 |
| Bending modulus | 40.0 | MPa | ISO 178 |
| 100 mm span | 50.0 | MPa | ASTM D790 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Pant tear resistance | 16.0 | N/mm | ISO 6383-1 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -40.0 | ℃ | ASTM D746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.3E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 2 mm in oil | 25 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 1 MHz | 2.50 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 2.0E-3 | IEC 60250 | |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 6.00 mm | V-0 | UL 94 | |
| Glowing wire flammability index | |||
| 3.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 3 mm | 775 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 24 | % | ISO 4589-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 65 to 75 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.010 | % | |
| Recommended injection volume | 30 to 70 | % | |
| Barrel rear temperature | 180 to 220 | °C | |
| Barrel middle temperature | 210 to 240 | °C | |
| Barrel front temperature | 220 to 250 | °C | |
| Nozzle temperature | 220 to 250 | °C | |
| Processing (melt) temperature | 220 to 250 | °C | |
| Mold temperature | 40 to 60 | °C | |
| Back pressure | 3.00 to 10.0 | MPa | |
| Screw speed | 30 to 80 | rpm | |
| Vent depth | 0.030 to 0.050 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 2.0 in/min |
| 3. 0.49 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |