Ultramid® B3S

soliao
2024年3月28日
Available in Soliao, PA6

About
An easy flowing, finely crystalline injection moulding grade for very fast processing. Parts produced include thin-walled technical parts (eg housing, fittings, grips, small parts and fixing clamps).&&

Product Description
Supplier	BASF
Generic	PA6
Material Status	Commercial: Active
Features	Good liquidity,Crystal,Quick molding cycle,Grease resistance
Availabilitys	Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.13	g/cm³	ISO 1183
Melt Volume Rate
275℃，5 kg	160	cm³/10min	ISO 1133
Shrinkage rate
MD	0.87	%	ISO 294-4
TD	1.0	%	ISO 294-4
Water absorption rate
Saturation, 23 ℃	9.0~10	%	ISO 62
Equilibrium, 23 ℃, 50% RH	2.6~3.4	%	ISO 62
Viscosity (96% H2SO4)	145	cm³/g	ISO 307

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level
1.60 mm	V-2		IEC 60695-11-10
Automotive materials (thickness>=1mm)	+		FMVSS 302

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
desiccation	3500	MPa	ISO 527-1-2
After adjustment	1200	MPa	ISO 527-1-2
tensile strength
Yield, drying	90	MPa	ISO 527-1-2
After mediation	45	MPa	ISO 527-1-2
Tensile strain
Yield, drying	4	%	ISO 527-1/2
Surrender, after mediation	20	%	ISO 527-1/2
Fracture, drying	10	%	ISO 527-1/2
Fracture, after drying	>50	%	ISO 527-1/2
Tensile creep modulus (1000 h, strain<=0.5%, 23 ° C)	1100	MPa	ISO 899-1
Bending modulus
desiccation	3000	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23 ℃, dry	250	kJ/m²	ISO 179/1eU
-30 ℃, dry	200	kJ/m²	ISO 179/1eU
23 ℃, dry	4	kJ/m²	ISO 179/1eA
23 ℃, after adjustment	50	kJ/m²	ISO 179/1eA
-30 ℃, dry	3	kJ/m²	ISO 179/1eA
Impact strength of cantilever beam notch
23℃	5		ISO 180-A
-30℃	5		ISO 180-A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa	65	℃	ISO 75-1/2
0.45 MPa	180	℃	ISO 75-1/2
Maximum operating temperature (short-term operation)	180	°C
Temperature index (50% loss of tensile strength)
5000hrs	97	°C	IEC 60216
20000hrs	87	°C	IEC 60216
Linear expansion coefficient (23~80 ℃)
MD	70~100	E-6/K	ISO 11359-1/-2
Thermal conductivity coefficient	0.33	W/m/K	DIN 52612-1
Specific heat capacity	1700	J/(kg*K)

Electrical performance	Nominal value	Unit	Test method
Relative permittivity
Dry, 1 MHz	3.3		IEC 60250
After adjustment, 1 MHz	7		IEC 60250
Dissipation factor
1 MHz, dry	300	E-4	IEC 60250
1 MHz, after adjustment	3000	E-4	IEC 60250
Volume resistivity
desiccation	1E15	ohms·cm	IEC 60093
After adjustment	1E12	ohms·cm	IEC 60093
Surface resistivity
After adjustment	1E+10	ohms	IEC 60093
Compared to the leakage tracing index
Solution A	600		IEC 60112

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	80	°C
Drying time	4.0	hr
Recommended maximum moisture content	0.15	%
Hopper temperature	80	°C
Barrel rear temperature	240	°C
Barrel middle temperature	250	°C
Barrel front temperature	260	°C
Nozzle temperature	260	°C
Processing (melt) temperature	250 to 270	°C
Mold temperature	40 to 60	°C
Screw Speed	< 300	mm/sec

Notes
1. Thickness: >=1mm
2. Typical properties: these are not to be construed as specifications.
3. Test box with central gating, dimensions of base (107471,5) mm, processing conditions: TM = 260°C, TW = 60°C
4. strain <= 0.5%, 23°C
5. 20000 h
6. 5000 h
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.