| Daelim Po1y® VL0005 is a Metallocene Linear Low Density Polyethylene product. It is available in Asia Pacific or Europe. Applications of Daelim Po1y® VL0005 include additive/masterbatch, film, food contact applications, industrial applications and packaging. Characteristics include: Good Sealability Antioxidant Clarity&& |
| Product Description | |
|---|---|
| Generic | mLLDPE |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good heat sealing,Inoxidizability,Low temperature heat sealing |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 5.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| TD, fracture, 22 µ m, blow molded film | 32.4 | MPa | ASTM D882 |
| MD, fracture, 22 µ m, blow molded film | 43.1 | MPa | ASTM D882 |
| Tensile strain | |||
| TD, fracture, 22 µ m, cast thin film | 600 | % | ASTM D882 |
| MD, fracture, 22 µ m, cast thin film | 380 | % | ASTM D882 |
| Drop hammer impact | |||
| 22 µ m, cast thin film | 350 | g | ASTM D1709-B |
| Sealing starting temperature | |||
| 22 µ m, cast thin film | 92.0 | ℃ | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 82.0 | ℃ | ASTM D1525 |
| Melting peak temperature | 91.0 | ℃ | ASTM D3418 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 22 µ m, cast thin film | 110 | ASTM D2457 | |
| Haze | |||
| 22 µ m, cast thin film | 0.50 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 250 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. HGT, 2.8 kg, 0.5 sec |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |