| About |
|---|
| Product Description | |
|---|---|
| Supplier | Audia |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.17 | g/cm³ | ASTM D792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 5.0 | MPa | ASTM D412 |
| Tensile modulus | |||
| 100% | 2.7 | MPa | ASTM D412 |
| 300% | 3.8 | MPa | ASTM D412 |
| elongation at break | 720 | % | ASTM D412 |
| Shore hardness | 72 | Shore A | ASTM D2240 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.5 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 70 – 90 | ℃ | |
| Drying time | 3 – 4 | hr | |
| Temperature of the rear section of the barrel | 220 – 240 | ℃ | |
| Temperature in the middle section of the barrel | 220 – 240 | ℃ | |
| Temperature of the front section of the material barrel | 230 – 250 | ℃ | |
| Nozzle temperature | 230 – 250 | ℃ | |
| Maximum melt temperature | 260 | ℃ | |
| Mold temperature | 10 – 60 | ℃ | |
| Injection pressure | 60% – 80%最大 | MPa | |
| Injection speed | 60% – 80%最大 | ||
| Maintaining pressure | 40% – 60%最大 | MPa | |
| Screw speed | 40 – 80 | rpm | |
| Back pressure | 10 – 30 | % | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |