About |
---|
Product Description | |
---|---|
Generic | Polycarbonate |
Material Status | Commercial: Negative |
Technical Data | |||
---|---|---|---|
PHYSICAL | Nominal value | Unit | Test method |
Melt Volume Rate | |||
300℃,12Kg | 10.3 | cm³/10min | ISO 1133 |
Density | 1.7 | g/cm³ | ISO 1183 |
Water absorption rate | |||
23℃,24hr | 0.19 | ||
Forming shrinkage rate | |||
MD | 0.57 | % | |
TD | 0.82 | % |
MECHANICAL | Nominal value | Unit | Test method |
---|---|---|---|
Tensile modulus | 2307 | MPa | ISO 527-1,-2 |
Tensile stress | |||
yield | 63.3 | MPa | ISO 527-1,-2 |
Tensile strain | |||
yield | 5 | ISO 527-1,-2 | |
fracture | 109 | ISO 527-1,-2 | |
Bending stress | 87 | MPa | ISO 176 |
Bending modulus | 2399 | MPa | ISO 176 |
THERMAL | Nominal value | Unit | Test method |
---|---|---|---|
Hot deformation temperature | |||
1.80 MPa | 121 | ℃ | ISO 75-1,-2 |
0.45 MPa | 136 | ℃ | ISO 75-1,-2 |
Linear coefficient of thermal expansion | |||
MD | 7.0E-5 | 1/℃ | ISO 11359-2 |
TD | 8.6E-5 | 1/℃ | ISO 11359-2 |
Electrical performance | Nominal value | Unit | Test method |
---|---|---|---|
Dielectric constant | |||
100 Hz | 2.91 | IEC 60250 | |
1 MHz | 2.55 | IEC 60250 | |
Dissipation factor | |||
100 Hz | 0.32142 | IEC 60250 | |
1 MHz | 0.01146 | IEC 60250 | |
Volume resistivity | 8.0E+16 | ohm·cm | IEC 60093 |
Surface resistivity | 1.74E+16 | ohm | IEC 60093 |
Dielectric strength | |||
2mm | 2475 | MV/M | IEC 60243-1 |
3mm | 1664 | MV/M | IEC 60243-1 |
FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
---|---|---|---|
Vertical burning characteristics | |||
10mm | V-2 | ISO 1210 | |
Vertical combustion characteristics | |||
1.5mm | V-2 | ISO 1210 | |
Vertical burning characteristics | |||
3.0mm | V-0 | ISO 1210 |
Notes |
---|
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |