| About |
|---|
| Product Description | |
|---|---|
| Material Status | Commercial: Active |
| Features | Excellent Processability,Solvent resistance |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Intrinsic viscosity | |||
| IV | 0.68 | dl/g | Internal Method |
| proportion | 1.34 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| 23℃ | 0.16 | % | ISO 62 |
| Forming shrinkage rate | 0.2-0.4 | % | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | 68 | ℃ | － |
| Glass transition temperature | 72 | ℃ | － |
| specific heat | 1.26 | KJ/℃.kg | ASTM D648 |
| vicat softening point | 76 | ℃ | ISO 306 |
| Thermal conductivity coefficient | 5.3E-4 | cal/s.cm.℃ | JIS K-7123 |
| Coefficient of thermal expansion | 7.1E-5 | /K | ASTM D-177 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 57 | Mpa | ISO 527 |
| Stretching rate | >300 | % | ISO 527 |
| Bending modulus | 2.5 | Gpa | ISO 178 |
| bending strength | 83 | Mpa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 2.2 | kJ/m² | ISO 179 |
| -30℃ | 2.1 | kJ/m² | ISO 179 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |