| PC2200R resin is a high flow (MFR = 22 at 300°C/1.2kg), heat stabilized, polycarbonate product with mold release designed for use in the general purpose molding market. It is available exclusively at www.sabicpc.com&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | High liquidity,Heat Stabilized,V-2 |
| Availabilitys | Europe,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile stress | |||
| Yield, Type I, 50 mm/min | 63 | MPa | ASTM D638 |
| Yield, 50 mm/min | 63 | MPa | ISO 527 |
| Tensile strain | |||
| Yield, Type I, 50 mm/min | 6 | % | ASTM D638 |
| Fracture, Type I, 50 mm/min | ＞70 | % | ASTM D638 |
| Yield, 50 mm/min | 6 | % | ISO 527 |
| Fracture, 50 mm/min | ＞70 | % | ISO 527 |
| Tensile modulus | |||
| 50 mm/min | 2350 | MPa | ASTM D638 |
| 1 mm/min | 2350 | MPa | ISO 527 |
| Bending stress | |||
| Yield, 1.3 mm/min, 50 mm span | 90 | MPa | ASTM D790 |
| Yield, 2 mm/min | 90 | MPa | ISO 178 |
| Bending modulus | |||
| 1.3 mm/min, 50 mm span | 2300 | MPa | ASTM D790 |
| 2 mm/min | 2300 | MPa | ISO 178 |
| Rockwell hardness | 120 | R Scale | ASTM D785，ISO 2039-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Instrument impact energy @ peak | |||
| 23℃ | 55 | J | ASTM D 3763 |
| Notched impact strength of cantilever beam | |||
| 23℃，80*10*3 | NB | kJ/m² | ISO 180/1U |
| -30℃，80*10*3 | NB | kJ/m² | ISO 180/1U |
| 23℃ | NB | J/m | ASTM D4812 |
| Impact strength of cantilever beam notch | |||
| 23℃，80*10*3 | 65 | kJ/m² | ISO 180-1A |
| -30℃，80*10*3 | 12 | kJ/m² | ISO 180-1A |
| 23℃ | 640 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| B/50 | 140 | ℃ | ASTM D1525，ISO 306 |
| Hot deformation temperature | |||
| 0.45 MPa，3.2 mm | 133 | ℃ | ASTM D648 |
| 1.8 MPa，3.2 mm | 122 | ℃ | ASTM D648 |
| 0.45 MPa Flatw 80*10*4 sp=64mm | 133 | ℃ | ISO 75/Bf |
| 1.8 MPa Flatw 80*10*4 sp=64mm | 122 | ℃ | ISO 75/Af |
| Linear expansion coefficient, flow | |||
| -40℃ ~95℃ | 7.E-05 | 1/℃ | ASTM E 831 |
| 23℃ ~ 80℃ | 7.E-05 | 1/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | |||
| 0.2 | W/m-°C | ASTM C177，ISO 8302 | |
| Ball pressure test | |||
| 125℃±2℃ | 通过 | IEC 60695-10-2 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.2 | ASTM D792 | |
| Mold shrinkage rate | |||
| On the stretching rod, flow | 0.5 – 0.7 | % | Internal Method |
| 3.2 mm, flowing | 0.5 – 0.7 | % | Internal Method |
| Melt Flow Rate | |||
| 300°C/1.2 kgf | 22 | g/10min | ASTM D1238 |
| Density | 1.2 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| 23 ℃, saturated | 0.35 | % | ASTM D570，ISO 62-1 |
| Melt Volume Rate | |||
| 300°C/1.2 kg | 21 | cm³/10min | ISO 1133 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 2.54 mm | 88 – 90 | % | ASTM D1003 |
| Haze | |||
| 2.54 mm | < 0.80 | % | ASTM D1003 |
| Refractive index | 1.586 | % | ASTM D542，ISO 489 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | >1.E+15 | Ω·cm | ASTM D257，IEC 60093 |
| Dielectric strength | |||
| 1.6 mm | 27 | kV/mm | ASTM D149，IEC 60243-1 |
| Relative permittivity | |||
| 60 Hz | 3 | ASTM D150，IEC 60250 | |
| 1 MHz | 3 | ASTM D150，IEC 60250 | |
| Dissipation factor | |||
| 60 Hz | 0.001 | ASTM D150，IEC 60250 | |
| 1 MHz | 0.01 | IEC 60250ASTM D150，IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| UL flame retardant rating | V-2 | UL 94 | |
| Flame retardant level | 1.5 | mm | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Drying time | 2 – 4 | hrs | |
| Maximum moisture content | 0.02 | % | |
| Melt Temperature | 280 – 300 | ℃ | |
| Nozzle temperature | 270 – 290 | ℃ | |
| Temperature of the rear section of the barrel | 260 – 280 | ℃ | |
| Temperature in the middle section of the barrel | 270 – 290 | ℃ | |
| Temperature of the front section of the material barrel | 280 – 300 | ℃ | |
| Hopper temperature | 60 – 80 | ℃ | |
| Mold temperature | 80 – 100 | ℃ | |
| drying temperature | 120 | ℃ | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. 2.0 in/min |
| 4. Type I, 2.0 in/min |
| 5. 0.051 in/min |
| 6. 0.079 in/min |
| 7. Yield |
| 8. 80*10*3 |
| 9. 80*10*4 mm |
| 10. Rate B (120°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |