| About |
|---|
| Product Description | |
|---|---|
| Supplier | DOMO |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ISO 1183 |
| Humidity absorption | |||
| 23℃，50% RH | 3.3-3.4 | % | ISO 62 |
| Water absorption | |||
| 24 hr，23℃ | 1.9-2 | % | ISO 62 |
| Saturation saturation | 9.1 | % | ISO 62 |
| Molding shrinkage | |||
| Parallel | 0.9-1.1 | % | ISO 294-4, 2577 |
| Normal | 1-1.2 | % | ISO 294-4, 2577 |
| Melt Volume Rate | |||
| 275℃，5Kg | 165 | cm³/10min | ISO 1133 |
| Viscosity number | |||
| 96% H2SO4 | 145 | cm³/g | ISO 307 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| Dry, 1 mm/min | 3200 | MPa | ISO 527-1/-2 |
| Wet Cond, 1 mm/min | 1000 | MPa | ISO 527-1/-2 |
| Tensile strain | |||
| 20 | % | ISO 527-1/-2 | |
| Break, wet cond, 50 mm/min | 50 | % | ISO 527-1/-2 |
| Yield, dry, 50 mm/min | 4 | % | ISO 527-1/-2 |
| Yield, wet cond, 50 mm/min | 20 | % | ISO 527-1/-2 |
| Tensile strength | |||
| 80 | MPa | ISO 527-1/-2 | |
| Wet Cond, 50 mm/min | 40 | MPa | ISO 527-1/-2 |
| Flexural modulus | |||
| Dry | 2800 | MPa | ISO 178 |
| Wet Cond | 900 | MPa | ISO 178 |
| Flexural strength | |||
| Dry | 105 | MPa | ISO 178 |
| Wet Cond | 35 | MPa | ISO 178 |
| Rockwell hardness | 120 | R Scale | ISO 2039/2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy impact strength of simply supported beams | |||
| -30 ℃, dry | 150 | KJ/m² | ISO 179/1eU |
| Charpy notched impact strength | |||
| 23 ℃, dry | 4.5 | kJ/m² | ISO 179/1eA |
| 23 ℃, moist cond | 20 | kJ/m² | ISO 179/1eA |
| Izod notched impact strength | |||
| 23 ℃, dry | 4.5 | KJ/m² | ISO 180/1A |
| 23 ℃, moist cond | 19 | KJ/m² | ISO 180/1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 221 | ℃ | ISO 11357-1 |
| Hot deformation temperature HDT | |||
| 0.45 MPa | 175 | ℃ | ISO 75 |
| 1.80 MPa | 65 | ℃ | ISO 75 |
| 50°C/h – 50N | 200 | ℃ | ISO 306 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1E16 | ohm·m | IEC 62631-3-1 |
| Surface resistivity | 1E14 | ohm | IEC 62631-3-1 |
| Compared tracking index | |||
| Solution A | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 0.75 mm | V2 | UL 94 | |
| Glow wire flammability index | |||
| 3.0 mm | 850 | ℃ | IEC 60695-2-12 |
| 1.0 mm | 750 | ℃ | IEC 60695-2-12 |
| Burning rate | <100 | mm/min | FMVSS 302 |
| Process Conditions | |||
|---|---|---|---|
| Injection molding | Nominal value | Unit | Test method |
| Drying temperature | 75-85 | ℃ | |
| Drying time | 2-4 | h | |
| Melt temperature | 230-250 | ℃ | |
| Mold temperature | 60-90 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |