| Thermoplastic Polyimide Extem* XH1015 Resin. Also UL rating 94V0 at 1.5 and 3.0.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | TPI |
| Material Status | Commercial: Active |
| Features | V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.31 | g/cm³ | ASTM D792 |
| Density | 1.31 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 337℃，6.60kg | 10 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 220℃，5 kg | 0.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 1.0 to 1.2 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 2.3 | % | ISO 62 |
| 23℃，24hr | 0.60 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3420 | MPa | ASTM D638 |
| Tensile modulus | 3100 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 74.0 | MPa | ISO 527-2/5 |
| fracture | 96.0 | MPa | ASTM D638 |
| yield | 101 | MPa | ISO 527-2/5 |
| yield | 103 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 10 | % | ASTM D638 |
| fracture | 7.0 | % | ISO 527-2/5 |
| yield | 6.0 | % | ISO 527-2/5 |
| yield | 7.0 | % | ASTM D638 |
| Bending modulus | 2870 | MPa | ISO 178 |
| 50 mm span | 3130 | MPa | ASTM D790 |
| bending strength | 120 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 168 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 43 | J/m | ASTM D256 |
| 23℃ | 4.2 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 1.8 MPa, unannealed, 64 mm span | 224 | ℃ | ISO 75-2/Af |
| 0.45 MPa, unannealed, 3.2 mm | 250 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 235 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 237 | ℃ | ASTM D648 |
| Vicat Softening Temp | 260 | ℃ | ASTM D1525 10 |
| Vicat Softening Temp | |||
| B50 | 250 | ℃ | ISO 306 |
| B120 | 248 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| TD：23~150℃ | 5.1E-5 | 1/℃ | ISO 11359-2 |
| MD：23~150℃ | 5.0E-5 | 1/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 175 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Drying time, maximum | 24 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 40 to 70 | % | |
| Barrel rear temperature | 360 to 385 | °C | |
| Barrel middle temperature | 370 to 400 | °C | |
| Barrel front temperature | 380 to 410 | °C | |
| Nozzle temperature | 375 to 405 | °C | |
| Processing (melt) temperature | 380 to 410 | °C | |
| Mold temperature | 150 to 175 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Screw speed | 70 to 100 | rpm | |
| Vent depth | 0.025 to 0.076 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 mm |
| 9. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |