| Injection-moulding grade containing 30% glass-fibres, for rigid,tough and dimensionally stable technical parts, used in applications with highest demands on hydrolysis resistance such es automotive connectors and housings for electronic units under the hood. The black colored product Ultradur® B4330 G6 HR BK15045 has a LS coloration (Laser Sensitive) and can be marked with Nd:YAG lasers.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Good Dimensional Stability,Hydrolysis stability,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.49 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 275℃，2.16 kg | 7.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 1.1 | % | ISO 294-4 |
| MD | 0.50 | % | ISO 294-4 |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.40 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.20 | % | ISO 62 |
| Viscosity number | 108 | cm³/g | ISO 307 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 8500 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 120 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 3.4 | % | ISO 527-2 |
| Bending modulus | 7860 | MPa | ISO 178 |
| bending strength | 190 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 8.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 14 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 65 | kJ/m² | ISO 179/1eU |
| 23℃ | 74 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 220 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 205 | ℃ | ISO 75-2/A |
| Melting temperature | 223 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD：23~80℃ | 2.0E-5 to 4.0E-5 | 1/℃ | ISO 11359-2 |
| specific heat | 1250 | J/kg/℃ | |
| Maximum operating temperature | |||
| short cycle operation | 210 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Compared to the leakage tracing index | |||
| Solution A | 400 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 120 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Hopper temperature | 80 | °C | |
| Barrel rear temperature | 250 | °C | |
| Barrel middle temperature | 255 | °C | |
| Barrel front temperature | 260 | °C | |
| Nozzle temperature | 260 | °C | |
| Processing (melt) temperature | 250 to 280 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Screw Speed | < 250 | mm/sec | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. solution 0,005 g/ml Phenole/1,2 Dichlorbenzol 1:1 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |