| XENOY ENH2900是一种半晶体，具有良好的尺寸稳定性，良好的流动、高冲击和优异的耐化学性能，是一种非溴化和非氯化阻燃型PC / PBT合金。通过注塑成型加工，适用于电气和电子等住房应用，符合UL 94 v – 0,v – 1和5VB火焰等级。 |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+PBT |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,Good liquidity,Solvent resistance |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | |||
| Fracture, Type I, 50 mm/min | 42 | MPa | ASTM D638 |
| Yield, Type I, 50 mm/min | 63 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, Type I, 50 mm/min | 65 | % | ASTM D638 |
| Yield, Type I, 50 mm/min | 4 | % | ASTM D638 |
| Tensile modulus | |||
| 5 mm/min | 2480 | MPa | ASTM D638 |
| bending strength | |||
| Yield, 50 mm span | 89 | MPa | ASTM D790 |
| Bending modulus | |||
| 1.3 mm/min，50mm跨距 | 2240 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 550 | J/m | ASTM D256 |
| Total energy of instrument impact | |||
| 23℃ | 65 | J | ASTM D 3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 102 | ℃ | ASTM D1525 |
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 78 | ℃ | ASTM D648 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.2 | ASTM D792 | |
| Shrinkage rate | |||
| MD：3.2 mm | 0.5 – 0.8 | % | Internal Method |
| Melt Flow Rate | |||
| 266℃，5.0kg | 26 | g/10min | ASTM D1238 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 94v-1 flame level assessment | 1.1 | mm | UL 94 |
| 94V-0 flame level assessment | 1.5 | mm | UL 94 |
| Flame retardant rating, 94-5VB flame rating evaluation | 2.5 | mm | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Drying temperature | 80 – 90 | °C | |
| Drying time | 3 – 4 | hrs | |
| Drying time (gradually increasing) | 8 | hrs | |
| Maximum water content | 0.04 | % | |
| Melt temperature | 245 – 275 | °C | |
| Nozzle temperature | 245 – 275 | °C | |
| Front Section Zone 3 Temperature | 245 – 275 | °C | |
| Temperature in Zone 2 of the middle section | 220 – 265 | °C | |
| Temperature in Zone 1 of the rear section | 220 – 265 | °C | |
| Mold temperature | 60 – 80 | °C | |
| Back pressure | 0.3 – 0.7 | MPa | |
| Screw speed | 40 – 70 | rpm | |
| Shoot to cylinder size | 30 – 80 | % | |
| Depth of exhaust groove | 0.038 – 0.076 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |