| About |
|---|
| Product Description | |
|---|---|
| Supplier | CHI MEI |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | V-0 |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Volume Rate | |||
| 300℃，1.2kg | 10 | cm³/10min | ISO 1133 |
| Specific Gravity | |||
| 23℃ | 1.2 | g/cm³ | ISO 1183 |
| Molding shrinkage | 0.4-0.6 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength | |||
| Yield yld, 50mm/min | 60 | MPa | ISO 527 |
| Broken BRK, 50mm/min | 70 | MPa | ISO 527 |
| Tensile Strain | |||
| 50mm/min | 120 | % | ISO 527 |
| Flexural Strength | |||
| 2mm/min | 90 | MPa | ISO 178 |
| Flexural Modulus | |||
| 2mm/min | 2300 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod Notched Impact strength | |||
| 23℃ | 60 | KJ/m² | ISO 180/1A |
| -30℃ | 15 | KJ/m² | ISO 180/1A |
| Charpy Notched Impact Strength | |||
| 23℃ | 60 | kJ/m² | ISO 179 |
| -30℃ | 15 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| 1kg，50℃/hr | 150 | ℃ | ISO 306 |
| 5kg，50℃/hr | 145 | ℃ | ISO 306 |
| Hot deformation temperature HDT | |||
| 125 | ℃ | ISO 75 | |
| 140 | ℃ | ISO 75 | |
| Coeff. of linear thermal expansion | 6.7E-5 | ISO 11359 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric Constant | |||
| 1MHz | 3 | ||
| Volume Resistance | 3.6E+14 | ohm·m | IEC 60093 |
| Surface Resistivity | 9.3E-14 | ohm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 1.5mm | V-0 | UL 94 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |