| Solef® 6020 PVDF homopolymer has very high viscosity for membranes and lithium batteries. It is available exclusively as powder.&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Material Status | Commercial: Active |
| Features | Ultra High Viscosity,Homopolymer |
| Availabilitys | North America,Asia Pacific,Europe,Africa & Middle East ,Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.75 to 1.80 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，21.6kg | < 2.0 | g/10min | ASTM D1238 |
| Water Absorption | |||
| 23℃，24hr | < 0.040 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | |||
| 23℃，2 mm | 1600 to 1700 | MPa | ASTM D638 |
| Tensile Strength | |||
| Broken BRK, 23 ℃, 2 mm | 25.0 to 50.0 | MPa | ASTM D638 |
| Yield yld, 23 ℃, 2 mm | 53.0 to 57.0 | MPa | ASTM D638 |
| Tensile Strain | |||
| Broken BRK, 23 ℃, 2 mm | 15 to 50 | % | ASTM D638 |
| Yield yld, 23 ℃, 2 mm | 5.0 to 10 | % | ASTM D638 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass Transition Temperature | -40.0 | ℃ | ASTM D4065 |
| Melting temperature | 171 to 175 | ℃ | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | |||
| DSC | 133 to 138 | ℃ | ASTM D3418 |
| Crystallization Heat | 47.0 to 52.0 | J/g | ASTM D3417 |
| Heat of Fusion | 57.0 to 66.0 | J/g | ASTM D3417 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | ASTM D257 |
| Volume Resistance | > 1.0E+14 | ohms·cm | ASTM D257 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type IV, 0.039 in/min |
| 3. Type IV, 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |