Udel® P-1700 polysulfones are tough, high-strength thermoplastics that are suitable for continuous use up to 300°F (149°C). Udel Film is resistant to oxidation and hydrolysis and withstand prolonged exposure to high temperatures and repeated sterilization. Udel® P-1700 polysulfone films are highly resistant to mineral acids, alkali and salt solutions. Their resistance to detergents and hydrocarbon oils is good, but they will be attacked by polar solvents such as ketones, chlorinated hydrocarbons, and aromatic hydrocarbons. Electrical properties of Udel® PSU films are stable over a wide temperature range and after immersion in water or exposure to high humidity. The film is transparent, a light amber color.&& |
Product Description | |
---|---|
Supplier | Solvay |
Generic | PSU |
Material Status | Commercial: Active |
Features | Good Rigidity,Good flexibility,Alkali resistant,Good disinfection,Hydrolysis stability,Gamma radiation,E-beam disinfection,Food contact compliance,Acidproof,High Heat Resistance,Inoxidizability |
Availabilitys | North America,Latin America,Asia Pacific,Europe |
Technical Data | |||
---|---|---|---|
PHYSICAL | Nominal value | Unit | Test method |
Density | 1.24 | g/cm³ | ASTM D792 |
Water absorption rate | |||
24hr | 0.30 | % | ASTM D570 |
MECHANICAL | Nominal value | Unit | Test method |
---|---|---|---|
Tear resistance | 7.4 | cN | ASTM D1004 |
film | Nominal value | Unit | Test method |
---|---|---|---|
film thickness | |||
test | |||
— | 30 | µm | |
— | 50 | µm | |
— | 130 | µm | |
Secant modulus | ASTM D882 | ||
MD | 2300 | MPa | ASTM D882 |
TD | 2370 | MPa | ASTM D882 |
tensile strength | ASTM D882 | ||
MD, yield | 68.0 | MPa | ASTM D882 |
TD, yield | 63.7 | MPa | ASTM D882 |
MD, fracture | 58.3 | MPa | ASTM D882 |
TD, fracture | 56.8 | MPa | ASTM D882 |
Tensile strain | ASTM D882 | ||
MD, yield | 5.5 | % | ASTM D882 |
TD, yield | 5.1 | % | ASTM D882 |
MD, fracture | 53 | % | ASTM D882 |
TD, fracture | 35 | % | ASTM D882 |
Drop hammer impact | 570 | g | ASTM D1709 |
Tear resistant vine ductility | 130 | gf | ASTM D1922 |
Area coefficient | 158 | ft²/lb/mil |
THERMAL | Nominal value | Unit | Test method |
---|---|---|---|
Hot deformation temperature | |||
1.8 MPa, unannealed | 174 | ℃ | ASTM D648 |
Linear coefficient of thermal expansion | |||
MD | 5.6E-5 | 1/℃ | ASTM D696 |
Glass transition temperature | 190 | ℃ |
Electrical performance | Nominal value | Unit | Test method |
---|---|---|---|
Volume resistivity | 3.0E+16 | ohms·cm | ASTM D257 |
Dielectric strength | 130 | kV/mm | ASTM D149 |
Dielectric constant | |||
1 kHz | 3.04 | ASTM D150 | |
Dissipation factor | |||
1 MHz | 6.0E-3 | ASTM D150 |
FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
---|---|---|---|
Extreme oxygen index | 26 | % | ASTM D2863 |
Notes |
---|
1. Typical properties: these are not to be construed as specifications. |
2. Impact properties |
3. Tear properties |
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |