| Product Description | |
|---|---|
| Supplier | Trinseo |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 4.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | |||
| Yield yld | 39 | MPa | ASTM D638 |
| Yield yld | 35 | MPa | ISO 527 |
| Broken BRK | 29 | MPa | ASTM D638 |
| Broken BRK | 27 | MPa | ISO 527 |
| Elongation at Break | |||
| 30 | % | ASTM D638 | |
| 35 | % | ISO 527 | |
| Flexural Modulus | 2000 | MPa | ASTM D790 |
| Flexural Strength | 60 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 40 | kJ/m² | ISO 179/1eA |
| Izod Notched Impact strength | 600 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa | 93 | ℃ | ASTM D648 |
| Vicat Softening Temperature | 96 | ℃ | ISO 306/B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 1.5 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 80-90 | ℃ | |
| Drying Time | 2-4 | hr | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |