| About |
|---|
| Product Description | |
|---|---|
| Generic | PA66 |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Specific Gravity | 1.8 | ASTM D792 | |
| Molding shrinkage | |||
| 3.2 mm | 0.1-0.3 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod Notched Impact strength | |||
| 3.2 mm | 320 | J/m | ASTM D256 |
| Izod Unnotched Impact strength of cantilever beam | |||
| 3.2 mm | 1068 | J/m | ASTM D256 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength | 221 | MPa | ASTM D638 |
| Tensile Elongation | 2.0 | % | ASTM D638 |
| Tensile Modulus | 17238 | MPa | ASTM D638 |
| Flexural Strength | 352 | MPa | ASTM D790 |
| Flexural Modulus | 16548 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.82 MPa | 237 | ℃ | ASTM D648 |
| Vicat Softening Temperature | 235 | ℃ | ASTM D1525 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 0.8 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Injection Pressure | 69-124 | MPa | |
| Melt Temperature | 277-299 | ℃ | |
| Mold Temperature | 66-107 | ℃ | |
| Drying Temperature | 79 | ℃ | |
| Drying Time | 4 | hr | |
| Moisture Content | 0.2 | % | |
| Dew Point | -18 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |