| About |
|---|
| Product Description | |
|---|---|
| Supplier | Celanese |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1490 | kg/m³ | ISO 1183 |
| Molding shrinkage | |||
| Parallel | 0.3 | % | ISO 294-4 |
| Normal | 0.9 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | 12800 | MPa | ISO 527 |
| Tensile Strength | |||
| Broken BRK | 135 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Broken BRK | 1.4 | % | ISO 527 |
| Flexural Modulus | 11200 | MPa | ISO 178 |
| Flexural Strength | 200 | MPa | ISO 178 |
| Poisson’s ratio | 0.33 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 8 | kJ/m² | ISO 179/1eA |
| -30℃ | 8 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 310 | ℃ | ISO 11357-3 |
| Glass Transition Temperature | |||
| 18 ° F/min, dry | 90 | ℃ | ISO 11357-2 |
| 18 ° F/min, moist cond | 45 | ℃ | ISO 11357-2 |
| Hot deformation temperature HDT | |||
| 1.8 MPa | 283 | ℃ | ISO 75-1/-2 |
| Relative Temperature Index (RTI) | |||
| Electrical | |||
| 30 mil | 140 | ℃ | UL-746B |
| 60 mil | 140 | ℃ | UL-746B |
| 120mil | 140 | ℃ | UL-746B |
| Mechanical impact | |||
| 30 mil | 115 | ℃ | UL-746B |
| 60 mil | 115 | ℃ | UL-746B |
| 120 mil | 120 | ℃ | UL-746B |
| Non mechanical impact strength | |||
| 30 mil | 125 | ℃ | UL-746B |
| 60 mil | 125 | ℃ | UL-746B |
| 120 mil | 130 | ℃ | UL-746B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 1.5 mm | V-0 | calss | IEC 60695-11-10 |
| 0.75 mm | V-0 | calss | IEC 60695-11-10 |
| Oxygen Index | 33 | % | ISO 4589-2 |
| Glow Wire Flammability Index (GWFI) | |||
| 30 mil | 960 | ℃ | IEC 60695-2-12 |
| 60 mil | 960 | ℃ | IEC 60695-2-12 |
| 120 mil | 960 | ℃ | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature (GWIT) | |||
| 30 mil | 775 | ℃ | IEC 60695-2-13 |
| 60 mil | 775 | ℃ | IEC 60695-2-13 |
| 120 mil | 850 | ℃ | IEC 60695-2-13 |
| FMVSS flame retardant rating | |||
| 1 mm | <80 | mm/min | FMVSS 302 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative permittivity | |||
| 100 Hz | 4.3 | IEC 62631-2-1 | |
| 1 MHz | 3.9 | IEC 62631-2-1 | |
| Dissipation Factor | |||
| 100 Hz | 50 | E-4 | IEC 62631-2-1 |
| 1 MHz | 110 | E-4 | IEC 62631-2-1 |
| 1 GHz | 110 | E-4 | ASTM D 2520 B |
| 10 GHz | 104 | E-4 | ASTM D 2520 B |
| Electric strength | 31 | kV/mm | IEC 60243-1 |
| Compared Tracking Index | |||
| 3.0 mm | 600 | PLC Code | IEC 60112 |
| Dielectric Constant | |||
| 1 GHz | 3.9 | ASTM D 2520 B | |
| 10 GHz | 3.9 | ASTM D 2520 B |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 100 | ℃ | |
| Drying Time | 6-8 | hr | |
| Maximum Moisture Content | ≤0.1 | % | |
| Min. Melt Temperature | 320 | ℃ | |
| Maximum Melt Temperature | 325 | ℃ | |
| Min Mold Temperature | 90 | ℃ | |
| Maximum Mold Temperature | 130 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |