| About |
|---|
| Product Description | |
|---|---|
| Supplier | Denka |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | North America,Europe,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.086 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 200℃，5.0kg | 5.2 | g/10min | ISO 1133 |
| 220℃，10.0kg | 76 | g/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 9 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa | 64.0 | ℃ | ISO 75-2/Af |
| Vicat Softening Temperature | 84 | ℃ | ISO 306/B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | HB | UL 94 |
| OPTICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Light Transmission | |||
| 2000 µm | 91.0 | % | ISO 13468-1 |
| Haze | |||
| 2000 µm | 2.6 | % | ISO 14782 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strain | ISO 527-2/5 | ||
| Yield yld, 50 mm/min | 47 | MPa | ISO 527-2/5 |
| Flexural Modulus | |||
| 2 mm/mim | 2250 | MPa | ISO 178 |
| Flexural Strength | |||
| 2 mm/min | 68 | MPa | ISO 178 |
| Rockwell hardness | |||
| M-level | 34 | ISO 2039-2 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |