| About |
|---|
| Ultradur S 4090 G6 LS BK15077 is a 30% glass reinforced PBT + ASA blend. It produces moldings with good surface finish and is resistant to chemicals and stress cracking. It has low shrinkage and warpage.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PBT+ASA |
| Material Status | Commercial: Active |
| Features | Low contractility,Solvent resistance,Laser engraving,High ESCR |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.47 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.40 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.20 | % | ISO 62 |
| Viscosity value | |||
| Reduced viscosity | 111.0 | ml/g | ISO 1628 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 23 ℃ | 120 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.3 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 8510 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 7.0 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 192 | ℃ | ISO 75-2/A |
| Melting temperature | |||
| DSC | 223 | ℃ | ISO 3146 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 to 120 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Processing (melt) temperature | 250 to 270 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Injection pressure | 3.50 to 12.5 | MPa | |
| Injection speed | Fast | ||
| Back pressure | < 1.00 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |