| About |
|---|
| Product Description | |
|---|---|
| Supplier | BASF |
| Material Status | Commercial: Active |
| Features | Elastic,Low temperature toughness,Weather resistance is good,Good wear resistance |
| Availabilitys | Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.24 | g/cm³ | ISO 1183 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| – | HB | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | NB | kJ/m² | ISO 179/1eA |
| -30℃ | 8.0 | kJ/m² | ISO 179/1eA |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 64 | ISO 868 | |
| Tensile Strength | |||
| ℃ | 55 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Fracture, 23 ℃ | 450 | % | ISO 527-2 |
| Tensile Modulus | |||
| 23℃ | 320 | MPa | ISO 527-2 |
| Tear strength | |||
| MD | 180 | KN/m | ISO 34-1 |
| Wear amount | 25 | mm³ | ISO 4649-A |
| Compression deformation | 35 | % | ISO 815 |
| Compression deformation | 50 | % | ISO 815 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion Molded | Nominal value | Unit | Test method |
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 110-120 | °C | |
| Drying Time | 2-3 | Hr | |
| Barrel Zone 1 Temperature | 170-210 | °C | |
| Barrel Zone 3 Temperature | 170-210 | °C | |
| Barrel Zone 5 Temperature | 170-210 | °C | |
| Die Temperature | 195-215 | °C | |
| Mold Temperature | 20-50 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |