| ELITE™ AT 6202 Enhanced Polyethylene Resin is an enhanced LLDPE ethylene-octene copolymer from Dow. This grade is a fully formulated sealant resin designed for demanding applications where hot tack strength is a key requirement. Main Characteristics High Hot Tack Strength Broad Hot Tack Window Low Heat Seal Initiation Temperature High Throughput Resin with excellent bubble stability Complies with: U.S. FDA FCN 424 Canadian HPFB No Objection EU, No 20/2011 Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | EPE |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.908 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.85 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Membrane puncture strength | |||
| 25 µm | 4.29 | J | Internal Method |
| Membrane puncture force | |||
| 25 µm | 54.3 | N | Internal Method |
| Membrane puncture resistance | |||
| 25 µm | 20.9 | J/cm³ | Internal Method |
| Secant modulus | ASTM D882 | ||
| 2% secant, MD: 25 µ m | 68.9 | MPa | ASTM D882 |
| 2% secant, TD: 25 µ m | 77.2 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield, 25 µ m | 7.93 | MPa | ASTM D882 |
| TD, yield, 25 µ m | 7.79 | MPa | ASTM D882 |
| MD, fracture, 25 µ m | 49.0 | MPa | ASTM D882 |
| TD, fracture, 25 µ m | 40.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 25 µ m | 450 | % | ASTM D882 |
| TD, fracture, 25 µ m | 600 | % | ASTM D882 |
| Drop hammer impact | |||
| 25 µm | 1000 | g | ASTM D1709-B |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：25 µm | 210 | g | ASTM D1922 |
| TD：25 µm | 430 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| DSC | 106 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45°，25.4 µm | 63 | ASTM D2457 | |
| Haze | |||
| 25.4 µm | 7.9 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| VFFS Hot Tack Window | 45°F (205-250 | Internal Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method B |
| 3. 2 mil coex film, 20/60/20 with MDPE core, sealant layer formulated with 10% LDPE and slip and AB. Tested on VFFS machine with 4 lbs fill weight, 0.25 second dwell time. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |