| About |
|---|
| Product Description | |
|---|---|
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,High impact resistance |
| Availabilitys | Europe,North America,Africa & Middle East ,Asia Pacific,Latin America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Melt Flow Rate | 2.0-8.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 1.4-2.0 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength | 24 | MPa | ASTM D638 |
| Tensile Elongation | >10.0 | % | ASTM D638 |
| Tensile Modulus | 896 | MPa | ASTM D638 |
| Flexural Modulus | 1172 | MPa | ASTM D790 |
| Flexural Strength | 33 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod Notched Impact strength | |||
| 3.2mm | 534 | J/m | ASTM D256 |
| Izod Unnotched Impact strength of cantilever beam | |||
| 3.2 mm | 无断裂 | ASTM D4812 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 0.45 MPa, unannealed | 87 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 58 | ℃ | ASTM D648 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric Constant | |||
| 1 MHz | 2.2 | ASTM D150 | |
| Dissipation Factor | |||
| 1 MHz | 3.2E-3 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 0.80 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 79 | °C | |
| Drying Time | 2.0 | hr | |
| Melt Temperature | 191-232 | °C | |
| Mold Temperature | 32-66 | °C | |
| Injection Pressure | 69-103 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |