| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PPS |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Shrinkage rate | |||
| MD | 0.2 | % | ISO 294-4 |
| TD | 0.5 | % | ISO 294-4 |
| Density | 1.65 | g/cm³ | ISO 1183 |
| Water absorption rate | 0.04 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| – | 15000 | MPa | ISO 527 |
| 120℃ | 6300 | MPa | ISO 527 |
| 160℃ | 4400 | MPa | ISO 527 |
| 200℃ | 3500 | MPa | ISO 527 |
| tensile strength | |||
| fracture | 190 | MPa | ISO 527 |
| Fracture, 120 ℃ | 85 | MPa | ISO 527 |
| Fracture, 160 ℃ | 62 | MPa | ISO 527 |
| Fracture, 200 ℃ | 50 | MPa | ISO 527 |
| Tensile strain | |||
| fracture | 2 | % | ISO 527 |
| Fracture, 120 ℃ | 4.5 | % | ISO 527 |
| Fracture, 160 ℃ | 5.1 | % | ISO 527 |
| Fracture, 200 ℃ | 5.8 | % | ISO 527 |
| Bending modulus | |||
| – | 14000 | MPa | ISO 178 |
| 120℃ | 5800 | MPa | ISO 178 |
| 160℃ | 4400 | MPa | ISO 178 |
| 200℃ | 3900 | MPa | ISO 178 |
| bending strength | 290 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 120 | ISO 2039-2 | |
| M-level | 100 | ISO 2039-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 60 | kJ/m² | ISO 179 |
| -30℃ | 70 | kJ/m² | ISO 179 |
| Charpy Notched Impact Strength | |||
| 23℃ | 10.5 | kJ/m² | ISO 179/1eA |
| -30℃ | 10 | kJ/m² | ISO 179/1eA |
| Notched impact strength of cantilever beam | 55 | KJ/m² | ISO 180/1U |
| Impact strength of cantilever beam notch | |||
| 23℃ | 11.5 | KJ/m² | ISO 180/1A |
| -40℃ | 10.5 | KJ/m² | ISO 180/1A |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |