| TECHNYL® A 60G1 V25 Black 2N is a polyamide 66 based on a non-halogenated flame retardant system, reinforced with 25% of glass fiber, heat stabilized, for injection moulding. This grade offers excellent flame retardancy properties (UL 94, 5VA, GWIT) combined with excellent processing, mechanical and electrical performance. It can withstand temperatures of 160°C for over 6000 hours and has a UL F1 rating for weatherability resistance at 0.8 mm.&& |
| Product Description | |
|---|---|
| Supplier | DOMO |
| Generic | PA66 |
| Material Status | Commercial: Negative |
| Features | V-0,Halogen free |
| Availabilitys | North America,Europe,Africa & Middle East |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.38 | g/cm³ | ISO 1183/A |
| f1 | UL 746C | ||
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| 23℃ | 9400 | MPa | ISO 527-2/1A |
| Tensile strength | |||
| Break, 23 ℃ | 130 | MPa | ISO 527-2/1A |
| Tensile Strain | |||
| Break, 23 ℃ | 2.0 | % | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 53 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 0.45 MPa, unannealed | 260 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 246 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 247 | ℃ | ISO 75-2/Af |
| Melting temperature | 263 | ℃ | ISO 11357-3 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 2.0E+15 | ohms | IEC 60093 |
| Volume resistivity | 6.0E+14 | ohms·cm | IEC 60093 |
| Electric strength | |||
| 0.8 mm | 35 | kV/mm | IEC 60243-1 |
| Compared tracking index | |||
| 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant rating Burning Behav | UL 94 | ||
| 0.80 mm | V-0 | UL 94 | |
| 1.60 mm | V-0 5VA | UL 94 | |
| 3.20 mm | V-0 5VA | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.80 mm | 960 | ℃ | IEC 60695-2-12 |
| 1.6 mm | 960 | ℃ | IEC 60695-2-12 |
| 3.2 mm | 960 | ℃ | IEC 60695-2-12 |
| IEC 60695-2-13 | |||
| 0.8 mm | 775 | ℃ | IEC 60695-2-13 |
| 1.6 mm | 775 | ℃ | IEC 60695-2-13 |
| Oxygen index | 33 | % | ISO 4589-2 |
| French Fire Index | F3 | NF F16-101 | |
| French Smoke Index | I3 | NF F16-101 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| European Railway Certification | EN 45545-2 | ||
| R22 | HL3 | EN 45545-2 | |
| R23 | HL3 | EN 45545-2 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Drying Temperature | 80 | °C | |
| Recommended maximum water content | 0.20 | % | |
| Injection molding cylinder temperature 1 | 265 to 275 | °C | |
| Injection molding cylinder temperature 2 | 265 to 275 | °C | |
| Injection molding cylinder temperature 3 | 270 to 280 | °C | |
| Mold temperature | 60 to 90 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |