| About |
|---|
| AS55-003 is a blow molding grade high density polyethylene copolymer containing an antistat additive. It provides a good balance of stiffness and stress crack resistance.&& |
| Product Description | |
|---|---|
| Supplier | ExxonMobil |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.954 | g/cm³ | ASTM D4883 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.30 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 100% non-ionic detergent | 30 | hr | ASTM D1693 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength | |||
| Yield yld | 28.0 | MPa | ASTM D638 |
| Flexural Modulus | |||
| 1% secant | 1000 | MPa | ASTM D790 |
| 2% secant | 850 | MPa | ASTM D790 |
| Shore hardness | 62 | Shore D | ASTM D2240 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Impact Strength | 190 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 0.45 MPa | 71 | ℃ | ASTM D648 |
| Vicat Softening Temperature | 127 | ℃ | ASTM D1525 |
| Melting peak temperature | 131 | ℃ | Internal Method |
| Crystallization peak | 118 | ℃ | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -20℃ | 5.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 9.0 | kJ/m² | ISO 179/1eA |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |