| Description High Heat Application Electric & Electronic Housing Automotives Interior & Exterior Housing (Garnish etc)&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High Heat Resistance,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ASTM D792 |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 7.0 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 220℃，10 kg | 7.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 to 0.70 | % | ISO 294-4 |
| MD：3.2 mm | 0.40 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 6.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 12 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃，3.2mm | 59 | J/m | ASTM D256 |
| -30℃，6.4mm | 49 | J/m | ASTM D256 |
| 23℃，3.2mm | 160 | J/m | ASTM D256 |
| 23℃，6.4mm | 140 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 6.0 | kJ/m² | ISO 180-1A |
| 23℃ | 13 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 102 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 4.0 mm | 93.0 | ℃ | ISO 75-2/Ae |
| 0.45 MPa, unannealed, 6.4 mm | 111 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 4.0 mm | 101 | ℃ | ISO 75-2/Be |
| Vicat Softening Temp | 112 | ℃ | ASTM D1525 6 |
| B50 | 112 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| TD：23~60℃ | 8.0E-5 to 9.0E-5 | 1/℃ | ISO 11359-2 |
| MD：23~60℃ | 8.0E-5 to 9.0E-5 | 1/℃ | ISO 11359-2 |
| Relative temperature index | |||
| Electrical performance | 60.0 | ℃ | UL 746 |
| Strength mechanical performance | 60.0 | ℃ | UL 746 |
| Impact mechanical performance | 60.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 23℃ | 1.5E+3 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 23 ℃，1 mm | 33 | kV/mm | ASTM D149 |
| Arc resistance | PLC 6 | ASTM D495 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2450 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Yield, 3.20 mm | 52.0 | MPa | ASTM D638 |
| yield | 54.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Fracture, 3.20 mm | 20 | % | ASTM D638 |
| Bending modulus | 2550 | MPa | ISO 178 |
| 3.20 mm | 2650 | MPa | ASTM D790 |
| bending strength | 82.0 | MPa | ISO 178 |
| 3.20 mm | 84.3 | MPa | ASTM D790 |
| Rockwell hardness | 114 | ISO 2039-2 | |
| R-level | 112 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.050 | % | |
| Barrel rear temperature | 180 to 200 | °C | |
| Barrel middle temperature | 200 to 220 | °C | |
| Barrel front temperature | 220 to 230 | °C | |
| Nozzle temperature | 220 to 230 | °C | |
| Processing (melt) temperature | 220 to 250 | °C | |
| Mold temperature | 40 to 60 | °C | |
| Back pressure | 0.981 to 2.94 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.59 in/min |
| 4. 0.079 in/min |
| 5. 120*10*4mm |
| 6. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |