| About |
|---|
| Product Description | |
|---|---|
| Generic | PS (HIPS) |
| Material Status | Commercial: Active |
| Features | Mechanical property,Good flexibility,high-rigidity |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 200℃，5kg | 3 | g/10min | ASTM D1238 |
| Spiral Flow | |||
| 220℃ | 44 | cm | ASTM D3123 |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Molding shrinkage | 0.4-0.7 | % | ASTM D955 |
| Water Absorption | 0.07 | % | ASTM D570 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat softening point | 100 | ℃ | ASTM D-1525 |
| Hot deformation temperature HDT | 80 | ℃ | ASTM D648 |
| Coeff. of linear thermal expansion | 9.05 | mm/℃ | ASTM D696 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod Notched Impact strength | 11.5 | KJ/m² | ASTM D256 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength | |||
| Yield yld | 32 | MPa | ASTM D638 |
| Elongation at Break | 45 | % | ASTM D638 |
| Flexural Modulus | 2300 | MPa | ASTM D790 |
| Rockwell hardness | 99 | R | ASTM D-785 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric Strength | 150 | kV/mm | ASTM D149 |
| Surface Resistivity | >1E14 | ohms | IEC 93 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion Molded | Nominal value | Unit | Test method |
| Barrel Zone 1 Temperature | 150-180 | ℃ | |
| Barrel Zone 2 Temperature | 170-210 | ℃ | |
| Barrel Zone 3 Temperature | 190-230 | ℃ | |
| Barrel Zone 4 Temperature | 200-240 | ℃ | |
| Nozzle temperature | 210-250 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |